Twenty-six SKUs across paint protection, colour, fibre, lighting, roof and glass — every one coated on the same line, to the same tolerances, from the same American TPU.
The number in every code is the number that matters: mil for paint protection, visible-light transmission for glass.
APEX for gloss, VELOUR for satin, ONYX for black, FLEX for the panels that fight back. All four share the same plasma-anchored top layer — the difference is the base and the thickness.
| SKU | Thickness | Gloss 60° | Haze | Tensile | Elongation | Warranty |
|---|---|---|---|---|---|---|
| APEX 10APEX · Gloss | 10.0 mil | ≥147 GU | 0.58% | ≥24.0 MPa | ≥390% | 10 years |
| APEX 9APEX · Gloss | 9.0 mil | ≥146 GU | 0.52% | ≥21.7 MPa | ≥364% | 10 years |
| APEX 8APEX · Gloss | 8.0 mil | ≥144 GU | 0.45% | ≥19.2 MPa | ≥348% | 7 years |
| VELOUR 8VELOUR · Matte | 8.0 mil | ≤18 GU | 8.20% | ≥26.0 MPa | ≥320% | 7 years |
| ONYX 8ONYX · Black gloss | 8.0 mil | ≥145 GU | — | ≥19.5 MPa | ≥310% | 7 years |
| FLEX 9.5FLEX · Gloss | 9.5 mil | ≥139 GU | 0.85% | ≥20.2 MPa | ≥358% | 5 years |
Typical values from production batch records. Full test data for every SKU is available on request.
Thickest clear coat in the range. Specified for full-body wraps on high-value vehicles and for markets with heavy stone-chip exposure.
| Total thickness | 10.0 mil (±0.5) |
|---|---|
| Top coat | Nano-ceramic self-cleaning hydrophobic, dual layer |
| Base film | Cast aliphatic polycaprolactone TPU |
| Gloss 60° | ≥147 GU |
| Haze | 0.58% |
| Tensile strength | ≥24.0 MPa |
| Elongation at break | ≥390% |
| Right-angle tear | ≥120 kN/m |
| 180° peel adhesion | 1,770 gf |
| Water contact angle | >95° |
| UV rejection | >99.0 |
| Yellowing | Grade 5 · xenon 1,200 h ΔYI ≤ 1.0 |
| Self-healing | Room temperature for light marks · 40 °C for deeper |
| Chemical resistance | 72 h: oxalic acid, calcium hydroxide, tar remover |
| Warranty | 10 years |
The volume SKU. Same top coat as APEX 10 with a marginally thinner base — the film most of our distributors standardise on.
| Total thickness | 9.0 mil (±0.5) |
|---|---|
| Top coat | Nano-ceramic self-cleaning hydrophobic, dual layer |
| Base film | Cast aliphatic polycaprolactone TPU |
| Gloss 60° | ≥146 GU |
| Haze | 0.52% |
| Tensile strength | ≥21.7 MPa |
| Elongation at break | ≥364% |
| Right-angle tear | ≥108 kN/m |
| 180° peel adhesion | 1,720 gf |
| Water contact angle | >95° |
| UV rejection | >99.0 |
| Yellowing | Grade 5 · xenon 1,200 h ΔYI ≤ 1.0 |
| Self-healing | Room temperature for light marks · 40 °C for deeper |
| Chemical resistance | 72 h: oxalic acid, calcium hydroxide, tar remover |
| Warranty | 10 years |
Entry point into the gloss range. Lowest haze of the three, which makes it the easiest sell on dark paint.
| Total thickness | 8.0 mil (±0.5) |
|---|---|
| Top coat | Nano-ceramic self-cleaning hydrophobic, dual layer |
| Base film | Cast aliphatic polycaprolactone TPU |
| Gloss 60° | ≥144 GU |
| Haze | 0.45% |
| Tensile strength | ≥19.2 MPa |
| Elongation at break | ≥348% |
| Right-angle tear | ≥90 kN/m |
| 180° peel adhesion | 1,680 gf |
| Water contact angle | >95° |
| UV rejection | >98.8 |
| Yellowing | Grade 5 · xenon 1,200 h ΔYI ≤ 1.0 |
| Self-healing | Room temperature for light marks · 40 °C for deeper |
| Chemical resistance | 72 h: oxalic acid, calcium hydroxide, tar remover |
| Warranty | 7 years |
Highest tensile and tear strength in the range — matte film is usually stretched harder during install, so it needs it.
| Total thickness | 8.0 mil (±0.5) |
|---|---|
| Top coat | Fine-textured matte anti-fouling, hydrophilic |
| Base film | Cast aliphatic polycaprolactone TPU |
| Gloss 60° | ≤18 GU |
| Haze | 8.20% |
| Tensile strength | ≥26.0 MPa |
| Elongation at break | ≥320% |
| Right-angle tear | ≥125 kN/m |
| 180° peel adhesion | 1,600 gf |
| Water contact angle | >88° |
| UV rejection | >98.8 |
| Yellowing | Grade 5 · xenon 1,200 h ΔYI ≤ 1.0 |
| Self-healing | Room temperature for light marks · 40 °C for deeper |
| Chemical resistance | 72 h: oxalic acid, calcium hydroxide, tar remover |
| Warranty | 7 years |
Opaque base, so haze is not a meaningful metric. Used for roof, pillar and trim work as well as full-body black.
| Total thickness | 8.0 mil (±0.5) |
|---|---|
| Top coat | High-black gloss, self-cleaning hydrophobic |
| Base film | Cast aliphatic polycaprolactone TPU |
| Gloss 60° | ≥145 GU |
| Haze | Opaque base |
| Tensile strength | ≥19.5 MPa |
| Elongation at break | ≥310% |
| Right-angle tear | ≥90 kN/m |
| 180° peel adhesion | 1,600 gf |
| Water contact angle | >92° |
| UV rejection | >99.2 |
| Yellowing | Grade 5 · xenon 1,200 h ΔYI ≤ 1.0 |
| Self-healing | Room temperature for light marks · 40 °C for deeper |
| Chemical resistance | 72 h: oxalic acid, calcium hydroxide, tar remover |
| Warranty | 7 years |
Conformability first. Priced for high-volume installation shops that cut a lot of film and cannot afford a failed bumper.
| Total thickness | 9.5 mil (±0.5) |
|---|---|
| Top coat | Nano anti-fouling hydrophilic, repairable |
| Base film | Cast aliphatic polycaprolactone TPU |
| Gloss 60° | ≥139 GU |
| Haze | 0.85% |
| Tensile strength | ≥20.2 MPa |
| Elongation at break | ≥358% |
| Right-angle tear | ≥118 kN/m |
| 180° peel adhesion | 1,700 gf |
| Water contact angle | >85° |
| UV rejection | >98.9 |
| Yellowing | Grade 5 · xenon 1,200 h ΔYI ≤ 1.0 |
| Self-healing | Room temperature for light marks · 40 °C for deeper |
| Chemical resistance | 72 h: oxalic acid, calcium hydroxide, tar remover |
| Warranty | 5 years |
Colour change on the same TPU core and the same adhesive as APEX — pigment instead of clarity, not a different film underneath.
Sixty shades are held in stock for immediate shipment: thirty gloss, thirty satin. Custom matches run from 30 rolls, with a physical strike-off approved before the line starts.
Twelve of sixty. Physical swatch books and roll-end samples are available to distributors at no charge.
Roofs, lights, screens, mirrors, livery and transit. Each of these started as a request from a distributor who could not find a film that behaved on that particular surface.
A real 3K twill weave embossed under a gloss or matte clear coat. Trim, roof, mirrors and interior parts.
Headlight and taillight film that takes stone chips and UV without crazing the polycarbonate underneath.
Sacrificial windshield layer for exotics and track cars. Optically clear, replaced instead of the screen.
A shade film for panoramic roofs — cuts the greenhouse effect without blocking the view out.
Printable PPF base for livery, fleet graphics and event wraps that still need stone-chip protection.
A sacrificial clear for transit, fleet and street furniture. Replaced instead of the paint underneath, and removed without solvent.
HALO for optical performance, AERO for signal-safe all-rounders, SOLA for volume, NOIR for custom black. Every figure below is measured on finished rolls, not on the master.
Spectral selectivity, not just darkness.
Eleven magnetron-sputtered layers of silver alloy, deposited under vacuum and then laminated to a clear PET core. It rejects heat at 1,400 nm without darkening the glass, which is the difference between a cool cabin and a dim one.
| SKU | VLT | UV | IR 940 nm | IR 1400 nm | TSER | SC | Haze |
|---|---|---|---|---|---|---|---|
| H70Windshield | 72% | 100% | 83% | 98% | 57% | 0.51 | 0.96 |
| H30Side / rear | 32% | 100% | 99% | 100% | 66% | 0.39 | 0.89 |
| H15Side / rear | 13% | 100% | 99% | 100% | 73% | 0.31 | 0.86 |
Signal-safe, all year round.
A graphene-loaded core with a dense optical stack on top. Non-metallic, so GPS, TPMS, e-toll and mobile signals pass straight through — the specification that decides most fleet and EV tenders.
| SKU | VLT | UV | IR 940 nm | IR 1400 nm | TSER | SC | Haze |
|---|---|---|---|---|---|---|---|
| A70Windshield | 73% | 100% | 93% | 98% | 46% | 0.62 | 1.46 |
| A30Side / rear | 31% | 100% | 96% | 99% | 58% | 0.47 | 1.30 |
| A15Side / rear | 15% | 100% | 97% | 99% | 65% | 0.40 | 1.22 |
The colour that stays put.
A dye system locked into the base rather than coated onto it. It is the film for dealers who fit a lot of cars and cannot afford a two-year-old tint that has gone purple in the rear screen.
| SKU | VLT | UV | IR 940 nm | IR 1400 nm | TSER | SC | Haze |
|---|---|---|---|---|---|---|---|
| S70Windshield | 70% | 99% | 40% | 44% | 41% | 0.67 | 1.32 |
| S30Side / rear | 30% | 99% | 45% | 49% | 48% | 0.57 | 1.28 |
| S15Side / rear | 14% | 99% | 48% | 52% | 54% | 0.51 | 1.25 |
Black on the outside, clear on the inside.
Five VLT grades from 50% down to 1%, colour-matched to a neutral black with no blue or red cast. Outside it reads as a single dark surface; inside you still have a usable mirror.
| SKU | VLT | UV | IR 940 nm | IR 1400 nm | TSER | SC | Haze |
|---|---|---|---|---|---|---|---|
| N50Side / rear | 49% | 100% | 98% | 99% | 54% | 0.53 | 0.97 |
| N30Side / rear | 29% | 100% | 99% | 99% | 62% | 0.44 | 0.94 |
| N15Side / rear | 14% | 100% | 99% | 100% | 68% | 0.37 | 0.92 |
| N05Side / rear | 5% | 100% | 99% | 100% | 74% | 0.30 | 0.90 |
| N01Privacy | 1% | 100% | 99% | 100% | 78% | 0.26 | 0.88 |
Construction of the paint protection range, and the physical format every series ships in.
| Base film | Cast aliphatic polycaprolactone TPU, USA |
|---|---|
| Top coat | Nano-ceramic self-cleaning hydrophobic, 12 µm, dual layer |
| Adhesive | Low-tack acrylic, pressure sensitive |
| Liner | PET, 50 µm, silicone coated |
| Yellowing | Grade 5 · xenon 1,200 h ΔYI ≤ 1.0 |
| Self-healing | Room temperature for light marks · 40 °C for deeper |
| Roll width | 1.52 m standard · up to 2.00 m on request |
|---|---|
| Roll length | 15 m / 30 m standard · custom |
| Core | 3 inch, printed or plain |
| Shelf life | 24 months, 5–30 °C, upright |
| Chemical resistance | 72 h immersion: oxalic acid, calcium hydroxide, tar remover |
| Certification | ISO 9001:2015 · IATF 16949 · REACH · RoHS |
Technical data sheets, MSDS and per-batch test reports are available for every SKU.